The Specificity of Forming the Structure and Mechanical Properties of АМг6л Alloy with the Enhanced Content of Silicon Admixtures after Casting and Heat Treatment

Автори

This paper studies the influence of silicon admixtures with the content up to 2 % on the phase-structural composition of АМг6л alloy after casting in the metallic form and heat treatment. Through experiments performed, we determine that it is possible to increase the content of silicon admixtures from 0,2 to 0,5 % for the АМг6л alloy used after casting in the metallic form. It can be increased under the conditions of conserving a high level of mechanical properties when the magnesium content in an alloy is within the limits of 6–6,5 %. Moreover, it is possible to increase the content of silicon admixtures from 0,2 to 1 % for the АМг6л alloy used after the heat treatment. It can also be increased solely under the conditions of conserving a high level of mechanical properties when the magnesium content in an alloy is within the limits of 6–6,5

Publication year: 
2010
Issue: 
1
УДК: 
661.74:669.14.046.554
С. 104—108, укр., Іл. 3. Табл. 7. Бібліогр.: 5 назв
References: 

1. Машиностроение. Энциклопедия. Цветные металлы и сплавы. Композиционные металлические материалы. Т. II / Под общ. ред. И.Н. Фридляндера. — М.: Металлургия, 2001. — 880 с.
2. Постников Н.С. Коррозионностойкие алюминиевые сплавы. — М.: Металлургия, 1976. — 303 с.
3. Мондольфо Л.Ф. Структура и свойства алюминиевых сплавов. — М.: Металлургия, 1979. — 640 с.
4. Колобнев И.Ф. Жаропрочность литейных алюминиевых сплавов. — М.: Металлургия, 1973. — 320 с.
5. Кулініч А.А., Гаврилюк В.П., Рябініна О.О., Доній О.М. Фазовоструктурний склад і механічні властивості сплаву Al-6 % Mg-2 % Zn-0,5 % Fe-0,5 % Si з добавками берилію після різних режимів відпалу // Наукові вісті НТУУ “КПІ”. — 2007. — № 3. — С. 101—104.

AttachmentSize
2010-1-13.pdf814.72 KB

Тематичні розділи журналу

,